Structures by: Wallbaum H. J.

Total: 24

TiZn3

TiZn3

Laves, F.Wallbaum, H.J.

Naturwissenschaften (1939) 27, 674-675

a=3.023Å   b=3.023Å   c=3.023Å

α=90°   β=90°   γ=90°

Titanium silicide (1/2)

Si2Ti

Laves, FWallbaum, H J

Zeitschrift fuer Kristallographie, Kristallgeometrie, Kristallphysik, Kristallchemie (-144,1977) (1939) 101, 78-93

a=8.236Å   b=4.773Å   c=8.523Å

α=90°   β=90°   γ=90°

Nickel titanium (3:1)

Ni3Ti

Laves, FWallbaum, H J

Zeitschrift fuer Kristallographie, Kristallgeometrie, Kristallphysik, Kristallchemie (-144,1977) (1939) 101, 78-93

a=5.096Å   b=5.096Å   c=8.304Å

α=90°   β=90°   γ=120°

Vanadium silicide (3/1)

SiV3

Wallbaum, H J

Zeitschrift fuer Metallkunde (1939) 31, 362-362

a=4.712(3)Å   b=4.712(3)Å   c=4.712(3)Å

α=90°   β=90°   γ=90°

AuPb2

AuPb2

Wallbaum, H.J.

Zeitschrift fuer Metallkunde (1943) 35, 218-221

a=7.324Å   b=7.324Å   c=5.655Å

α=90°   β=90°   γ=90°

KNa2

KNa2

Laves, F.Wallbaum, H.J.

Zeitschrift fuer Anorganische und Allgemeine Chemie (1942) 250, 110-120

a=7.49Å   b=7.49Å   c=12.29Å

α=90°   β=90°   γ=120°

InNi2

InNi2

Laves, F.Wallbaum, H.J.

Zeitschrift fuer Angewandte Mineralogie (1942) 4, 17-46

a=4.179Å   b=4.179Å   c=5.131Å

α=90°   β=90°   γ=120°

Os2Zr

Os2Zr

Wallbaum, H.J.

Naturwissenschaften (1942) 30, 149-149

a=5.189Å   b=5.189Å   c=8.526Å

α=90°   β=90°   γ=120°

Re2Zr

Re2Zr

Wallbaum, H.J.

Naturwissenschaften (1942) 30, 149-149

a=5.261Å   b=5.261Å   c=8.593Å

α=90°   β=90°   γ=120°

Ru2Zr

Ru2Zr

Wallbaum, H.J.

Naturwissenschaften (1942) 30, 149-149

a=5.141Å   b=5.141Å   c=8.509Å

α=90°   β=90°   γ=120°

Pt3Ti

Pt3Ti

Wallbaum, H.J.

Naturwissenschaften (1943) 31, 91-91

a=3.897Å   b=3.897Å   c=3.897Å

α=90°   β=90°   γ=90°

NbSi2

NbSi2

Wallbaum, H.J.

Zeitschrift fuer Metallkunde (1941) 33, 378-381

a=4.794Å   b=4.794Å   c=6.589Å

α=90°   β=90°   γ=120°

Ta Ge2

Ge2Ta

Wallbaum, H.J.

Naturwissenschaften (1944) 32, 76-76

a=4.958Å   b=4.958Å   c=7.65Å

α=90°   β=90°   γ=120°

Ta Si2

Si2Ta

Wallbaum, H.J.

Zeitschrift fuer Metallkunde (1941) 33, 378-381

a=4.773Å   b=4.773Å   c=6.552Å

α=90°   β=90°   γ=120°

Mo3Zr

Mo3Zr

Wallbaum, H.J.

Naturwissenschaften (1942) 30, 149-149

a=4.942Å   b=4.942Å   c=4.942Å

α=90°   β=90°   γ=90°

Ga3Ti

Ga3Ti

Wallbaum, H.J.

Zeitschrift fuer Metallkunde (1942) 34, 118-119

a=3.931Å   b=3.931Å   c=8.109Å

α=90°   β=90°   γ=90°

Pb2Pd

Pb2Pd

Wallbaum, H.J.

Zeitschrift fuer Metallkunde (1943) 35, 218-221

a=6.849Å   b=6.849Å   c=5.833Å

α=90°   β=90°   γ=90°

Ga3Zr

Ga3Zr

Wallbaum, H.J.

Zeitschrift fuer Metallkunde (1942) 34, 118-119

a=3.971Å   b=3.971Å   c=8.729Å

α=90°   β=90°   γ=90°

Pb2Rh

Pb2Rh

Wallbaum, H.J.

Zeitschrift fuer Metallkunde (1943) 35, 218-221

a=6.651Å   b=6.651Å   c=5.853Å

α=90°   β=90°   γ=90°

Cu1.74In0.96

Cu1.74In0.96

Laves, F.Wallbaum, H.J.

Zeitschrift fuer Angewandte Mineralogie (1942) 4, 17-46

a=4.269Å   b=4.269Å   c=5.239Å

α=90°   β=90°   γ=120°

Fe2 Ge

Fe1.715Ge0.975

Laves, F.Wallbaum, H.J.

Zeitschrift fuer Angewandte Mineralogie (1942) 4, 17-46

a=4.031Å   b=4.031Å   c=5.022Å

α=90°   β=90°   γ=120°

Co2Ti

Co2Ti

Wallbaum, H.J.Witte, H.

Zeitschrift fuer Metallkunde (1939) 31, 185-187

a=6.704Å   b=6.704Å   c=6.704Å

α=90°   β=90°   γ=90°

Sn2Pt

PtSn2

Wallbaum, H. J.

Zeitschrift fur Metallkunde (1943) 35, 200-201

a=6.413Å   b=6.413Å   c=6.413Å

α=90°   β=90°   γ=90°

Insizwaite

Bi2Pt

Wallbaum, H. J.

Zeitschrift fur Metallkunde (1943) 35, 200-201

a=6.683Å   b=6.683Å   c=6.683Å

α=90°   β=90°   γ=90°